Causes of Excessive Slag in the Ferrosilicon Smelting Furnace
1. In ferrosilicon smelting, sometimes the furnace is short of carbon for a long time, and a large amount of excess silica dissolves to form viscous slag, which is not easy to eliminate.
2. Due to the high charge level, the depth of electrode inserted into the charge becomes shallow, the furnace temperature is low, and the slag is not easy to be removed. In particular, the electric furnace with a small capacity is more likely to produce this phenomenon, resulting in too much slag in the furnace.
3. Although the amount of slag is small when smelting ferrosilicon, the slag shall be brought out as far as possible during tapping to make the electrode deeply inserted. If you don't pay attention to slag, it will cause too much slag in the furnace for a long time.
4. Poor quality of raw materials, such as too high ash content in coke or too much soil on the surface of silica, will also increase the amount of slag.
Hazards of Excessive Slag in the Smelting Furnace:
1. The bottom of the furnace rises, it is difficult to insert deeply after clicking, it shrinks after drying, the air permeability of the charge surface deteriorates, and the furnace condition deteriorates.
2. The furnace bottom temperature is low, the taphole is not easy to open, the furnace hole is not unblocked, the flow rate of molten iron is slow, and the amount of iron is less.
Hani Tech is a Hot Rolling Mill manufacturing company working mainly in the area of the bar and wire rod mills, high-speed wire rod mills, high-speed rebar rolling mills, TMT rolling mills, flying shear, cold strip rolling mill, reheating furnace, induction furnace, intermediate frequency furnace, electric arc furnace, ladle refining furnace, blast furnace, continuous casting machine.
Free send inquiry to stella@hanrm.com if any needs.
Whatsapp/Wechat:+8615877652925
Email: stella@hanrm.com stellarollingmill@gmail.com
Website: https://www.hanrm.com
.jpg)
没有评论:
发表评论